Pure and silica-containing Al hydroxide aerogels were prepared by the supercritical drying method. The samples were later calcined, giving rise to alumina and Si-Al mixed oxides. The materials were characterized from the points of view of their bulk and surface structures. The Si-free material before calcination is well-crystallized boehmite that converts to gamma-alumina by calcination. The silica-containing hydroxides are composed of boehmite layers with silicates in the interlayer region. The resulting mixed oxides present silica essentially in the bulk. The surface structure of alumina seems poorly sensitive to silica addition. Surface silanol groups appear only for SiO2 more than 4%. No Bronsted acidity appears. Silica addition allows mixed oxides with higher surface areas to be obtained. (C) 1997 Academic Press.
Characterization of silica-containing aluminum hydroxide and oxide aerogels RID A-1095-2008
Trombetta M;
1997-01-01
Abstract
Pure and silica-containing Al hydroxide aerogels were prepared by the supercritical drying method. The samples were later calcined, giving rise to alumina and Si-Al mixed oxides. The materials were characterized from the points of view of their bulk and surface structures. The Si-free material before calcination is well-crystallized boehmite that converts to gamma-alumina by calcination. The silica-containing hydroxides are composed of boehmite layers with silicates in the interlayer region. The resulting mixed oxides present silica essentially in the bulk. The surface structure of alumina seems poorly sensitive to silica addition. Surface silanol groups appear only for SiO2 more than 4%. No Bronsted acidity appears. Silica addition allows mixed oxides with higher surface areas to be obtained. (C) 1997 Academic Press.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.